| Electrochemical investigation on the hydrogen permeation behavior of 7075-T6 Al alloy and its influence on stress corrosion cracking | |
| Zheng, Chuan-bo1,2; Yan, Bing-hao1; Zhang, Ke3; Yi, Guo1 | |
| 2015-07-01 | |
| 发表期刊 | INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS
 |
| 卷号 | 22期号:7页码:729-737 |
| 文章类型 | Article |
| 摘要 | The hydrogen permeation behavior and stress corrosion cracking (SCC) susceptibility of precharged 7075-T6 Al alloy were investigated in this paper. Devanthan-Stachurski (D-S) cell tests were used to measure the apparent hydrogen diffusivity and hydrogen permeation current density of specimens immersed in 3.5wt% NaCl solution. Electrochemical experiment results show that the SCC susceptibility is low during anodic polarization. Both corrosion pits and hydrogen-induced cracking are evident in scanning electron microscope images after the specimens have been charging for 24 h. |
| 关键词 | Aluminum Alloys Hydrogen Permeation Hydrogen Embrittlement Stress Corrosion Cracking |
| DOI | 10.1007/s12613-015-1128-5 |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000357696100009 |
| 引用统计 | |
| 文献类型 | 期刊论文 |
| 条目标识符 | http://ir.qdio.ac.cn/handle/337002/48990 |
| 专题 | 海洋环境腐蚀与生物污损重点实验室 |
| 作者单位 | 1.Jiangsu Univ Sci & Technol, Sch Mat Sci & Engn, Zhenjiang 212003, Peoples R China 2.Chinese Acad Sci, Inst Oceanol, Key Lab Marine Environm Corros & Biofouling, Qingdao 266071, Peoples R China 3.China Petr Pipeline Bur, Langfang 065000, Peoples R China |
| 第一作者单位 | 中国科学院海洋研究所 |
| 推荐引用方式 GB/T 7714 | Zheng, Chuan-bo,Yan, Bing-hao,Zhang, Ke,et al. Electrochemical investigation on the hydrogen permeation behavior of 7075-T6 Al alloy and its influence on stress corrosion cracking[J]. INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS,2015,22(7):729-737. |
| APA | Zheng, Chuan-bo,Yan, Bing-hao,Zhang, Ke,&Yi, Guo.(2015).Electrochemical investigation on the hydrogen permeation behavior of 7075-T6 Al alloy and its influence on stress corrosion cracking.INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS,22(7),729-737. |
| MLA | Zheng, Chuan-bo,et al."Electrochemical investigation on the hydrogen permeation behavior of 7075-T6 Al alloy and its influence on stress corrosion cracking".INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS 22.7(2015):729-737. |
| 条目包含的文件 | ||||||
| 文件名称/大小 | 文献类型 | 版本类型 | 开放类型 | 使用许可 | ||
| Electrochemical inve（4080KB） | 期刊论文 | 出版稿 | 限制开放 | CC BY-NC-SA | 浏览 | |
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论