Electrochemical investigation on the hydrogen permeation behavior of 7075-T6 Al alloy and its influence on stress corrosion cracking
Zheng, Chuan-bo1,2; Yan, Bing-hao1; Zhang, Ke3; Yi, Guo1
2015-07-01
发表期刊INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS
卷号22期号:7页码:729-737
文章类型Article
摘要The hydrogen permeation behavior and stress corrosion cracking (SCC) susceptibility of precharged 7075-T6 Al alloy were investigated in this paper. Devanthan-Stachurski (D-S) cell tests were used to measure the apparent hydrogen diffusivity and hydrogen permeation current density of specimens immersed in 3.5wt% NaCl solution. Electrochemical experiment results show that the SCC susceptibility is low during anodic polarization. Both corrosion pits and hydrogen-induced cracking are evident in scanning electron microscope images after the specimens have been charging for 24 h.
关键词Aluminum Alloys Hydrogen Permeation Hydrogen Embrittlement Stress Corrosion Cracking
DOI10.1007/s12613-015-1128-5
收录类别SCI
语种英语
WOS记录号WOS:000357696100009
引用统计
被引频次:12[WOS]   [WOS记录]     [WOS相关记录]
文献类型期刊论文
条目标识符http://ir.qdio.ac.cn/handle/337002/48990
专题海洋腐蚀与防护研究发展中心
作者单位1.Jiangsu Univ Sci & Technol, Sch Mat Sci & Engn, Zhenjiang 212003, Peoples R China
2.Chinese Acad Sci, Inst Oceanol, Key Lab Marine Environm Corros & Biofouling, Qingdao 266071, Peoples R China
3.China Petr Pipeline Bur, Langfang 065000, Peoples R China
推荐引用方式
GB/T 7714
Zheng, Chuan-bo,Yan, Bing-hao,Zhang, Ke,et al. Electrochemical investigation on the hydrogen permeation behavior of 7075-T6 Al alloy and its influence on stress corrosion cracking[J]. INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS,2015,22(7):729-737.
APA Zheng, Chuan-bo,Yan, Bing-hao,Zhang, Ke,&Yi, Guo.(2015).Electrochemical investigation on the hydrogen permeation behavior of 7075-T6 Al alloy and its influence on stress corrosion cracking.INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS,22(7),729-737.
MLA Zheng, Chuan-bo,et al."Electrochemical investigation on the hydrogen permeation behavior of 7075-T6 Al alloy and its influence on stress corrosion cracking".INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS 22.7(2015):729-737.
条目包含的文件
文件名称/大小 文献类型 版本类型 开放类型 使用许可
Electrochemical inve(4080KB)期刊论文出版稿开放获取CC BY-NC-SA浏览 请求全文
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Zheng, Chuan-bo]的文章
[Yan, Bing-hao]的文章
[Zhang, Ke]的文章
百度学术
百度学术中相似的文章
[Zheng, Chuan-bo]的文章
[Yan, Bing-hao]的文章
[Zhang, Ke]的文章
必应学术
必应学术中相似的文章
[Zheng, Chuan-bo]的文章
[Yan, Bing-hao]的文章
[Zhang, Ke]的文章
相关权益政策
暂无数据
收藏/分享
文件名: Electrochemical investigation on the hydrogen permeation behavior of 7075-T6 Al alloy and its influence on stress corrosion cracking.pdf
格式: Adobe PDF
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。