Corrosion behavior of steel in Chengdao offshore oil exploitation area
Li, Y; Hou, B; Li, H; Zhang, J
AbstractFrom September 1992 to September 1995, the corrosion behavior of three marine steels was studied in Chengdao offshore area by means of individually and electro-connectedly hanging plates in order to provide data for anticorrosion design of oil-exploitation structures there. The variation trend of corrosion rate with exposure time showed that the variation curves and degrees of three steels were generally identical and had nothing to do with the exposure time. The whole change trend of corrosion rates in three years showed that the corrosion rates of 20(#) steel were nearly identical in different positions, each of which was a little lower than that of 16 Mn steel specimens in corresponding positions, also was lower than that of; steel specimens in tidal zone and immersion zone. Although 20(#) steel corroded rapidly at first, its corrosion rate has a decreasing trend in the long-term service. Therefore, 20(#) steel is feasible to be applied for a long time in various marine zones, especially nearby the low tidal line and immersion zone. The results of A(3) steel, 16 Mn steel and 20(#) steel by means of electrically connected hanging plate in three years indicated that the corrosion of the steel specimens in the splash zone was the most severe as the result of dry-wet cycle and macrocell effect. Specimens in the other positions corroded mildly, and that in tidal zone corroded most slowly. The corrosion rate of 20(#) steel was the highest among the three steels in the test, and the corrosion rates of A(3) steel and 16 Mn steel were identical on the whole. When the specimens were hanged electro-connectedly, the macrocell effect generally tended to increase with exposure time. The. highest corrosion rate of A(3) steel in the splash zone in the three years was about 0.278 mm/a, while that of 16 Mn steel was about 0.321 mm/a, and that of 20(#) steel was 0.330 mm/a or so. In contrast, the corrosion rate of the steels in the tidal zone was the lowest in three years, which were 0.052 mm/a (A(3) steel), 0.048 mm/a (16 Mn steel) and 0.040 mm/a (20(#) steel).
Indexed BySCI
WOS IDWOS:000220947100008
Citation statistics
Cited Times:11[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
AffiliationChinese Acad Sci, Inst Oceanol, Dept Marine Corros, Qingdao 266071, Peoples R China
Recommended Citation
GB/T 7714
Li, Y,Hou, B,Li, H,et al. Corrosion behavior of steel in Chengdao offshore oil exploitation area[J]. MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION,2004,55(4):305-309.
APA Li, Y,Hou, B,Li, H,&Zhang, J.(2004).Corrosion behavior of steel in Chengdao offshore oil exploitation area.MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION,55(4),305-309.
MLA Li, Y,et al."Corrosion behavior of steel in Chengdao offshore oil exploitation area".MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION 55.4(2004):305-309.
Files in This Item:
File Name/Size DocType Version Access License
Corrosion behavior o(130KB)期刊论文出版稿开放获取ODC PDDLView Application Full Text
Related Services
Recommend this item
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Li, Y]'s Articles
[Hou, B]'s Articles
[Li, H]'s Articles
Baidu academic
Similar articles in Baidu academic
[Li, Y]'s Articles
[Hou, B]'s Articles
[Li, H]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Li, Y]'s Articles
[Hou, B]'s Articles
[Li, H]'s Articles
Terms of Use
No data!
Social Bookmark/Share
File name: Corrosion behavior of steel in Chengdao offshore oil exploitation area.pdf
Format: Adobe PDF
All comments (0)
No comment.

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.