Chromate passivation of hot dipped Zn25Al alloy coatings

	Chromate passivation of hot dipped Zn25Al alloy coatings
	Li, Y ; Wang, H; Hou, B ; Feng, F ; Wei, X
	2001
发表期刊	BRITISH CORROSION JOURNAL
卷号	36 期号:1 页码:56-58
文章类型	Article
摘要	A low concentration chromate passivation treatment has been successfully applied to a new type of hot dipped Zn25Al alloy coating, and the corrosion resistance of the chromate passive film has been assessed using the copper accelerated acetic salt spray (CASS) test, electrochemical measurements, and sea water immersion testing. The results showed that the corrosion resistance of the Zn25Al alloy coating was significantly better after the chromate passivation treatment. X-ray photoelectron spectroscopy (XPS) and Auger electron spectroscopy (AES) analyses showed that the composition (at.-%) of the low concentration chromate passive film was: 5.5S-3.4Na-11.8C-7.9Ti-41.6O-13.7Cr-16.0Zn. Aluminium was not found in the film, which is attributed to the dissolution behaviour of the Zn25Al alloy coating in acidic chromate solution.
收录类别	SCI
语种	英语
WOS记录号	WOS:000169445900007
引用统计	被引频次：9[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.qdio.ac.cn/handle/337002/32982
专题	海洋环境腐蚀与生物污损重点实验室
作者单位	1.Chinese Acad Sci, Inst Oceanol, Qingdao 266071, Peoples R China 2.Luoyang Ship Mat Res Inst, Qingdao Branch, Qingdao 266071, Peoples R China 3.NE Univ Technol, Shenyang 110006, Peoples R China
推荐引用方式 GB/T 7714	Li, Y,Wang, H,Hou, B,et al. Chromate passivation of hot dipped Zn25Al alloy coatings[J]. BRITISH CORROSION JOURNAL,2001,36(1):56-58.
APA	Li, Y,Wang, H,Hou, B,Feng, F,&Wei, X.(2001).Chromate passivation of hot dipped Zn25Al alloy coatings.BRITISH CORROSION JOURNAL,36(1),56-58.
MLA	Li, Y,et al."Chromate passivation of hot dipped Zn25Al alloy coatings".BRITISH CORROSION JOURNAL 36.1(2001):56-58.

条目包含的文件
文件名称/大小	文献类型	版本类型	开放类型	使用许可
Chromate passivation（93KB）	期刊论文	出版稿	限制开放	ODC PDDL	浏览