Effect of sulphide pollutants on mild steel corrosion in 3.5% NaCl solutions

doi:10.1179/147842209X12476568584188

	Effect of sulphide pollutants on mild steel corrosion in 3.5% NaCl solutions
	Wang, X. T.; Hou, B. R.
	2010-02-01
发表期刊	CORROSION ENGINEERING SCIENCE AND TECHNOLOGY
卷号	45 期号:1 页码:57-60
文章类型	Article
摘要	Corrosion behaviour of mild steel in 3.5% NaCl solution containing sulphide pollutants was investigated using potentiodynamic polarisation measurement, electrochemical impedance spectroscopy and scanning electron microscopy. Reaction and mechanism of the corrosion process were discussed. The study shows that sulphide concentration had a remarkable effect on pitting corrosion. Sulphide pollutants exhibited inhibition effect with passive film in the initial stage of corrosion. When the passive film breaks down, sulphide would accelerate the corrosion process.
关键词	Sulphide Pollutants Mild Steel Corrosion Pitting
DOI	10.1179/147842209X12476568584188
收录类别	SCI
语种	英语
WOS记录号	WOS:000275034300008
引用统计	被引频次：4[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.qdio.ac.cn/handle/337002/32801
专题	海洋环境腐蚀与生物污损重点实验室
作者单位	Chinese Acad Sci, Inst Oceanol, Qingdao 266071, Peoples R China
第一作者单位	中国科学院海洋研究所
推荐引用方式 GB/T 7714	Wang, X. T.,Hou, B. R.. Effect of sulphide pollutants on mild steel corrosion in 3.5% NaCl solutions[J]. CORROSION ENGINEERING SCIENCE AND TECHNOLOGY,2010,45(1):57-60.
APA	Wang, X. T.,&Hou, B. R..(2010).Effect of sulphide pollutants on mild steel corrosion in 3.5% NaCl solutions.CORROSION ENGINEERING SCIENCE AND TECHNOLOGY,45(1),57-60.
MLA	Wang, X. T.,et al."Effect of sulphide pollutants on mild steel corrosion in 3.5% NaCl solutions".CORROSION ENGINEERING SCIENCE AND TECHNOLOGY 45.1(2010):57-60.

条目包含的文件
文件名称/大小	文献类型	版本类型	开放类型	使用许可
Effect of sulphide p（214KB）	期刊论文	出版稿	限制开放	ODC PDDL	浏览