Corrosion of mild steel in different granularity seabed sediment saturated with seawater | |
Jizhou, D; Baorong, H; Yanliang, H; Huyuan, S; Yan, L; Shide, M | |
2002-11-01 | |
发表期刊 | MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION |
ISSN | 0947-5117 |
卷号 | 53期号:11页码:845-849 |
文章类型 | Article |
摘要 | In order to investigate the corrosion of pipeline materials in Seabed Sediment (SBS) environment, weight-loss and electrochemical measurements in saturated sand and mud cells with seawater were performed for a simulation. The used electrochemical measurements included linear polarization resistance (LPR) and potentiodynamic scanning measurement. It was showed that the corrosion rate of mild steel in the present condition was lower than the corrosion rate of other marine environment corrosion zones of it; that the granularity of SBS could affect the corrosion behavior greatly; that with increasing grain size of SBS, the corrosion rate increased. Integrated over the results of the weight loss and polarization curves, the oxygen diffusion (oxygen as a depolarizant agent) mechanism was proposed and discussed.; In order to investigate the corrosion of pipeline materials in Seabed Sediment (SBS) environment, weight-loss and electrochemical measurements in saturated sand and mud cells with seawater were performed for a simulation. The used electrochemical measurements included linear polarization resistance (LPR) and potentiodynamic scanning measurement. It was showed that the corrosion rate of mild steel in the present condition was lower than the corrosion rate of other marine environment corrosion zones of it; that the granularity of SBS could affect the corrosion behavior greatly; that with increasing grain size of SBS, the corrosion rate increased. Integrated over the results of the weight loss and polarization curves, the oxygen diffusion (oxygen as a depolarizant agent) mechanism was proposed and discussed. |
学科领域 | Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering |
收录类别 | SCI |
语种 | 英语 |
WOS记录号 | WOS:000179426600007 |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | http://ir.qdio.ac.cn/handle/337002/2336 |
专题 | 海洋环境腐蚀与生物污损重点实验室 |
作者单位 | 1.Chinese Acad Sci, Inst Oceanol, Qingdao 266071, Peoples R China 2.Chinese Acad Sci, Grad Sch, Beijing 100039, Peoples R China |
推荐引用方式 GB/T 7714 | Jizhou, D,Baorong, H,Yanliang, H,et al. Corrosion of mild steel in different granularity seabed sediment saturated with seawater[J]. MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION,2002,53(11):845-849. |
APA | Jizhou, D,Baorong, H,Yanliang, H,Huyuan, S,Yan, L,&Shide, M.(2002).Corrosion of mild steel in different granularity seabed sediment saturated with seawater.MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION,53(11),845-849. |
MLA | Jizhou, D,et al."Corrosion of mild steel in different granularity seabed sediment saturated with seawater".MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION 53.11(2002):845-849. |
条目包含的文件 | ||||||
文件名称/大小 | 文献类型 | 版本类型 | 开放类型 | 使用许可 | ||
duan-Corrosion of mi(131KB) | 限制开放 | -- | 浏览 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论