Sulphate Corrosion Mechanism of Ultra-High-Performance Concrete (UHPC) Prepared with Seawater and Sea Sand
Sun, Xin1,2; Li, Tianyu3; Shi, Fangying4; Liu, Xiaoyan3; Zong, Yingxia5; Hou, Baorong1; Tian, Huiwen1,2
2022-03-01
发表期刊POLYMERS
卷号14期号:5页码:21
通讯作者Li, Tianyu(brhou@qdio.ac.cn) ; Hou, Baorong(brhou@qdio.ac.cn) ; Tian, Huiwen(tianhuiwen@qdio.ac.cn)
摘要The lack of river sand is becoming increasingly serious. In this study, we consider how to use sea sand to prepare innovative construction and building materials with excellent mechanical and durability properties. Sulphate corrosion causes expansion, cracking and spalling of concrete, resulting in the reduction or even loss of concrete strength and cementation force. In this paper, artificial seawater, sea sand, industrial waste, steel fiber and polycarboxylate superplasticizer were used to prepare ultra-high-performance polymer cement mortar (SSUHPC), and the sulphate corrosion mechanism was investigated. The strength and cementation force of mortar on the SSUHPC surface decreased and flaked off with the development of sulphate erosion, and the steel fiber rusted and fell off. A 3D model was established based on X-ray computed tomography (X-CT), and the results showed that SSUHPC maintained excellent internal structural characteristics despite severe sulphate erosion on the surface. Mercury intrusion porosimetry (MIP), scanning electron microscopy (SEM) and X-ray diffraction (XRD) techniques were adopted to investigate the sulphate corrosion mechanism of SSUHPC. We found a transition zone within 1-5 mm of the surface of SSUHPC. The Vickers hardness of mortar in this area was increased by 5~15%, and the porosity was reduced to 3.8489%. Obvious structural damage did not occur in this area, but a high content of gypsum appeared. UHPC prepared with seawater sea sand was found to have better sulphate resistance than that prepared with freshwater river sand, which supports the development and utilization of sea sand in concrete.
关键词sea sand polymer cement mortar UHPC sulphate corrosion material characterization X-CT
DOI10.3390/polym14050971
收录类别SCI
语种英语
资助项目Shandong Key Laboratory of Corrosion Science, China ; National Natural Science Foundation of China[41827805] ; National Natural Science Foundation of China[51879093]
WOS研究方向Polymer Science
WOS类目Polymer Science
WOS记录号WOS:000768475500001
出版者MDPI
引用统计
被引频次:14[WOS]   [WOS记录]     [WOS相关记录]
文献类型期刊论文
条目标识符http://ir.qdio.ac.cn/handle/337002/178237
专题海洋环境腐蚀与生物污损重点实验室
通讯作者Li, Tianyu; Hou, Baorong; Tian, Huiwen
作者单位1.Chinese Acad Sci, Inst Oceanol, Key Lab Marine Environm Corros & Biofouling, Qingdao 266071, Peoples R China
2.Univ Chinese Acad Sci, 19 A Yuquan Rd, Beijing 100049, Peoples R China
3.Hohai Univ, Coll Mech & Mat, Nanjing 210098, Peoples R China
4.Hohai Univ, Coll Environm, Nanjing 210098, Peoples R China
5.Qingdao Univ Sci & Technol, Coll Chem & Mol Engn, Qingdao 266071, Peoples R China
第一作者单位中国科学院海洋研究所
通讯作者单位中国科学院海洋研究所
推荐引用方式
GB/T 7714
Sun, Xin,Li, Tianyu,Shi, Fangying,et al. Sulphate Corrosion Mechanism of Ultra-High-Performance Concrete (UHPC) Prepared with Seawater and Sea Sand[J]. POLYMERS,2022,14(5):21.
APA Sun, Xin.,Li, Tianyu.,Shi, Fangying.,Liu, Xiaoyan.,Zong, Yingxia.,...&Tian, Huiwen.(2022).Sulphate Corrosion Mechanism of Ultra-High-Performance Concrete (UHPC) Prepared with Seawater and Sea Sand.POLYMERS,14(5),21.
MLA Sun, Xin,et al."Sulphate Corrosion Mechanism of Ultra-High-Performance Concrete (UHPC) Prepared with Seawater and Sea Sand".POLYMERS 14.5(2022):21.
条目包含的文件
文件名称/大小 文献类型 版本类型 开放类型 使用许可
polymers-14-00971-v2(8150KB)期刊论文出版稿限制开放CC BY-NC-SA浏览
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Sun, Xin]的文章
[Li, Tianyu]的文章
[Shi, Fangying]的文章
百度学术
百度学术中相似的文章
[Sun, Xin]的文章
[Li, Tianyu]的文章
[Shi, Fangying]的文章
必应学术
必应学术中相似的文章
[Sun, Xin]的文章
[Li, Tianyu]的文章
[Shi, Fangying]的文章
相关权益政策
暂无数据
收藏/分享
文件名: polymers-14-00971-v2.pdf
格式: Adobe PDF
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。