Effect of the coexistence of albumin and H2O2 on the corrosion of biomedical cobalt alloys in physiological saline | |
Xu, Weichen1,3,4,5; Zhang, Binbin1,3,4; Yang, Lihui1,3,4; Ni, Qiancheng1,3; Li, Yantao1,3,4; Yu, Fei2 | |
2019-10-17 | |
发表期刊 | RSC ADVANCES |
卷号 | 9期号:57页码:32954-32965 |
通讯作者 | Yu, Fei(feiyu@qdu.edu.cn) |
摘要 | The corrosion of Co-28Cr-6Mo and Co-35Ni-20Cr-10Mo, as biomedical alloys, has been investigated for effects of typical species (albumin and H2O2) in physiological saline, with their coexistence explored for the first time. Electrochemical and long term immersion tests were carried out. It was found that Co alloys were not sensitive to the presence of albumin alone, which slightly promoted anodic dissolution of Co-35Ni-20Cr-10Mo without noticeably affecting Co-28Cr-6Mo and facilitated oxide film dissolution on both alloys. H2O2 led to a clear drop in corrosion resistance, favouring metal release and surface oxide formation and inducing much thicker but less compact oxide films for both alloys. The coexistence of both species resulted in the worst corrosion resistance and most metal release, while the amount and composition of surface oxide remained at a similar level as in the absence of both. The effect of H2O2 inducing low compactness of surface oxides should prevail on deciding the poor corrosion protection ability of passive film, while albumin simultaneously promoted dissolution or inhibited formation of oxides due to H2O2. Corrosion resistance was consistently lower for Co-35Ni-20Cr-10Mo under each condition, the only alloy where the synergistic effect of both species was clearly demonstrated. This work suggests that the complexity of the environment must be considered for corrosion resistance evaluation of biomedical alloys. |
DOI | 10.1039/c9ra05699h |
收录类别 | SCI |
语种 | 英语 |
资助项目 | Natural Science Foundation of Shandong Province, China[ZR2017BEM025] ; Natural Science Foundation of Shandong Province, China[ZR2019QEM011] ; National Natural Science Foundation of China[51701101] ; Applied Basic Research Program of Nantong, China[GY12017020] ; Applied Basic Research Program of Qingdao, China[17-1-1-41-jch] ; Natural Science Foundation of Shandong Province, China[ZR2017BEM025] ; Natural Science Foundation of Shandong Province, China[ZR2019QEM011] ; National Natural Science Foundation of China[51701101] ; Applied Basic Research Program of Nantong, China[GY12017020] ; Applied Basic Research Program of Qingdao, China[17-1-1-41-jch] |
WOS研究方向 | Chemistry |
WOS类目 | Chemistry, Multidisciplinary |
WOS记录号 | WOS:000496135200003 |
出版者 | ROYAL SOC CHEMISTRY |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | http://ir.qdio.ac.cn/handle/337002/163874 |
专题 | 海洋环境腐蚀与生物污损重点实验室 |
通讯作者 | Yu, Fei |
作者单位 | 1.Chinese Acad Sci, Inst Oceanol, Key Lab Marine Environm Corros & Biofouling, Qingdao 266071, Shandong, Peoples R China 2.Qingdao Univ, Med Coll, Inst Translat Med, Qingdao 266021, Shandong, Peoples R China 3.Pilot Natl Lab Marine Sci & Technol, Open Studio Marine Corros & Protect, Qingdao 266237, Shandong, Peoples R China 4.Chinese Acad Sci, Ctr Ocean Megasci, Qingdao 266071, Shandong, Peoples R China 5.Chinese Acad Sci, Res Dev Ctr Marine Sci & Technol, Inst Oceanol, Nantong 226019, Peoples R China |
第一作者单位 | 海洋环境腐蚀与生物污损重点实验室; 中国科学院海洋大科学研究中心; 中国科学院海洋研究所 |
推荐引用方式 GB/T 7714 | Xu, Weichen,Zhang, Binbin,Yang, Lihui,et al. Effect of the coexistence of albumin and H2O2 on the corrosion of biomedical cobalt alloys in physiological saline[J]. RSC ADVANCES,2019,9(57):32954-32965. |
APA | Xu, Weichen,Zhang, Binbin,Yang, Lihui,Ni, Qiancheng,Li, Yantao,&Yu, Fei.(2019).Effect of the coexistence of albumin and H2O2 on the corrosion of biomedical cobalt alloys in physiological saline.RSC ADVANCES,9(57),32954-32965. |
MLA | Xu, Weichen,et al."Effect of the coexistence of albumin and H2O2 on the corrosion of biomedical cobalt alloys in physiological saline".RSC ADVANCES 9.57(2019):32954-32965. |
条目包含的文件 | ||||||
文件名称/大小 | 文献类型 | 版本类型 | 开放类型 | 使用许可 | ||
Effect of the coexis(1536KB) | 期刊论文 | 出版稿 | 限制开放 | CC BY-NC-SA | 浏览 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论