Keyword电偶腐蚀 海洋环境腐蚀 Eh40钢 B10铜合金 硫酸盐还原菌 假交替单胞菌

对海洋工程材料而言,海洋是复杂而苛刻的腐蚀环境,电偶腐蚀难以避免,但海洋微生物对电偶腐蚀影响的研究报道较少。本论文以船舶用材料EH40钢和B10铜合金为研究对象,主要采用电化学测量方法表面分析技术等手段探究了假交替单胞菌(Pseudoalteromonas sp.,P.sp.)、硫酸盐还原菌(Sulfate-reducting bacteria,SRB)以及P.sp.与SRB的混合菌对EH40/B10电偶腐蚀的影响机制。主要结果如下:

(1)研究了P.sp.对EH40/B10电偶腐蚀的影响机制。结果发现,P.sp.的存在降低了EH40/B10的电偶腐蚀速率。在无菌体系中,电偶电流密度稳定在12 μA/cm2左右;在P.sp.体系中,电偶电流密度稳定在0.1 μA/cm2左右,比在无菌体系中的电偶电流密度降低约100倍。在P.sp.体系中EH40和B10表面都覆盖了一层生物膜,并且P.sp.体系中的溶解氧含量远低于无菌体系中的溶解氧含量。同时,P.sp.的生命活动使得溶液pH降低,偏酸性P.sp.对EH40/B10电偶腐蚀的抑制作用与P.sp.的呼吸耗氧及生物膜的形成密切相关。尽管P.sp.的生命活动使得溶液pH降低,但其对腐蚀的促进作用要小于保护性生物膜和呼吸耗氧对腐蚀的抑制作用。

(2)探讨了无氧环境中SRB对EH40/B10电偶腐蚀的影响。结果发现,SRB对EH40/B10电偶腐蚀效应影响微弱,但显著促进了EH40、B10的自腐蚀速率。EH40/B10的电偶电流密度在无菌和SRB体系中都维持在0.8 μA/cm2以下,但相较于无菌体系中EH40和B10表面基本无腐蚀产物形成、Rct很大,SRB使得EH40、B10表面覆盖腐蚀产物,且去除腐蚀产物后出现点蚀坑,Rct降低超过2个数量级。并且SRB的存在使得电偶电流密度在第5天和第9天为负值,EH40/B10电偶对极性发生反转,这可能源自SRB对EH40和B10不同腐蚀作用机制的差异。


Other Abstract

Seawater is complex and harsh corrosion environment for marine engineering materials, and galvanic corrosion is difficult to avoid. But few reports have addressed the influence of marine microorganisms on the galvanic corrosion. In this thesis, EH40 steel and B10 copper alloy commonly used on ships were taken as the research objects, and the electrochemical measurement methods and surface analysis technologies were utilized to study the influence mechanism of Pseudoalteromonas sp. (P.sp.), sulfate-reducing bacteria (SRB), and mixed bacteria (P.sp. + SRB) on galvanic corrosion. The main results are as followed:

(1) The influence mechanism of P.sp. on the galvanic corrosion of EH40/B10 was studied. The presence of P.sp. reduced the galvanic corrosion rate of EH40/B10. In the abiotic system, the galvanic current density stablized around 12 μA/cm2. In the P.sp. system, the galvanic current density stablized around 0.1 μA/cm2, which was about 100 times lower than that in the abiotic system. Biofilms were found on the surface of EH40 and B10 in the P.sp. system, and the dissolved oxygen concentration in the P.sp. system was much lower than that in the abiotic system. Meanwhile, the presence of P.sp. reduced the pH of solution. The galvanic corrosion of EH40/B10 was inhibited by P.sp., which is believed to be closely associated with oxygen depletion and biofilm formation. Although the decrease in pH is harmful for corrosion inhibition, its influence is much smaller than those of oxygen consumption and biofilm protection.

(2) The influence of SRB on EH40/B10 galvanic corrosion in anaerobic environment was discussed. SRB had quite limited effect on EH40/B10 galvanic corrosion, but significantly promoted the self-corrosion rate of EH40 and B10. The galvanic current density of EH40/B10 was maintained below 0.8 μA/cm2 in both abiotic and SRB systems. EH40 and B10 basically had no corrosion products on the surface and the Rct was very large in the abiotic system, but the introduction of SRB led to numerous corrosion products and pitting pits after removing. Furthermore, Rct decreased by more than 2 orders of magnitude. The galvanic current density was negative on day 5 and day 9 due to the presence of SRB, and the polarity of EH40/B10 was reversed, which may be due to the difference in corrosion mechanisms of SRB on EH40 and B10.

(3) The influence mechanism of the mixture of P.sp. and SRB on EH40/B10 galvanic corrosion was studied. The influence of P.sp. and SRB on EH40/B10 galvanic corrosion could be divided into two stages, which was closely related to the synergistic growth and metabolism of the two bacteria. At the beginning of immersion when P.sp. multiplied and consumed oxygen, the couple potential shifted negatively rapidly and the galvanic current density decreased sharply, which was similar to the case in the P.sp. system. Then, P.sp. declined and created an anoxic environment which facilitated the growth of the anaerobic microorganism SRB. Accordingly, the galvanic potential gradually increased until it stabilized, and the galvanic current density increased firstly and then decreased. Meanwhile, the Rct of EH40 steel maintained at a low level, similar to that of the SRB system.

Subject Area海洋科学
MOST Discipline Catalogue理学::海洋科学
Document Type学位论文
Recommended Citation
GB/T 7714
高洁艳. 海洋典型微生物对EH40/B10电偶腐蚀的影响[D]. 中国科学院海洋研究所. 中国科学院大学,2019.
Files in This Item:
File Name/Size DocType Version Access License
毕业论文-高洁艳201628006812(6169KB)学位论文 延迟开放CC BY-NC-SAView 2023-7-1后可获取
Related Services
Recommend this item
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[高洁艳]'s Articles
Baidu academic
Similar articles in Baidu academic
[高洁艳]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[高洁艳]'s Articles
Terms of Use
No data!
Social Bookmark/Share
File name: 毕业论文-高洁艳201628006812028.pdf
Format: Adobe PDF
All comments (0)
No comment.

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.