Effect of anti-corrosive performance, roughness and chemical composition of pre-treatment layer on the overall performance of the paint system on cold-rolled steel
Gao, Xiang1; Li, Weihua1,2; Ma, Houyi3
2017-11-25
发表期刊SURFACE & COATINGS TECHNOLOGY
卷号329页码:19-28
文章类型Article
摘要Many fundamental researches about the effect of some basic properties of a pre-treatment layer, such as anti-corrosive performance, surface roughness and chemical composition on the overall performance of paint systems were investigated. Three kinds of pre-treatment layers: bare polyacrylic acid (PAA) layer, Mo based layer and Mo doped PAA layer were deposited on cold-rolled steel surfaces through immersing the steel samples in the corresponding solution. The electrochemical measurements results indicated that after been treated in PAA solution, the steels became vulnerable to corrosion and the Mo based layer and Mo doped PAA layer could improve the corrosion resistance of steel to a certain degree. The values of root-mean-square roughness of the bare steel, bare PAA layer, Mo based layer and Mo doped PAA layer were 15.0 nm, 11.3 nm, 13.0 run and 59.1 nm, respectively. The corresponding values of arithmetic average roughness of the samples were 16.9 nm, 10.5 nm, 9.1 nm and 41.0 nm, respectively. The spectroscopy results indicated that the surface of the bare PAA and Mo doped PAA layer covered steels contained abundant COON groups and the composition of Mo based layer covered steel surface was mainly oxides. According to the impact test and neutral salt spray test results, the corrosion mitigation performance, microstructure and chemical composition of the pre-treatment layer could all affect the overall performance of the paint system. All the results indicated that the anti-corrosive performance was not the only index, the microstructure and chemical composition also needed to be considered in the development of a new generation pre-treatment layer.
关键词Pre-treatment Layer Polyacrylic Acid Corrosion Resistance Adhesion Paint System
DOI10.1016/j.surfcoat.2017.09.029
收录类别SCI
语种英语
WOS记录号WOS:000414115300003
引用统计
被引频次:2[WOS]   [WOS记录]     [WOS相关记录]
文献类型期刊论文
版本出版稿
条目标识符http://ir.qdio.ac.cn/handle/337002/143052
专题海洋腐蚀与防护研究发展中心
作者单位1.Chinese Acad Sci, Inst Oceanol, Key Lab Marine Environm Corros & Biofouling, Qingdao 266071, Peoples R China
2.Qingdao Technol Univ, Cooperat Innovat Ctr Engn Construct & Safety Shan, Qingdao 266033, Peoples R China
3.Shandong Univ, Sch Chem & Chem Engn, State Educ Minist, Key Lab Colloid & Interface Chem, Jinan 250100, Shandong, Peoples R China
推荐引用方式
GB/T 7714
Gao, Xiang,Li, Weihua,Ma, Houyi. Effect of anti-corrosive performance, roughness and chemical composition of pre-treatment layer on the overall performance of the paint system on cold-rolled steel[J]. SURFACE & COATINGS TECHNOLOGY,2017,329:19-28.
APA Gao, Xiang,Li, Weihua,&Ma, Houyi.(2017).Effect of anti-corrosive performance, roughness and chemical composition of pre-treatment layer on the overall performance of the paint system on cold-rolled steel.SURFACE & COATINGS TECHNOLOGY,329,19-28.
MLA Gao, Xiang,et al."Effect of anti-corrosive performance, roughness and chemical composition of pre-treatment layer on the overall performance of the paint system on cold-rolled steel".SURFACE & COATINGS TECHNOLOGY 329(2017):19-28.
条目包含的文件
文件名称/大小 文献类型 版本类型 开放类型 使用许可
Effect of anti-corro(1532KB)期刊论文出版稿开放获取CC BY-NC-SA浏览 请求全文
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Gao, Xiang]的文章
[Li, Weihua]的文章
[Ma, Houyi]的文章
百度学术
百度学术中相似的文章
[Gao, Xiang]的文章
[Li, Weihua]的文章
[Ma, Houyi]的文章
必应学术
必应学术中相似的文章
[Gao, Xiang]的文章
[Li, Weihua]的文章
[Ma, Houyi]的文章
相关权益政策
暂无数据
收藏/分享
文件名: Effect of anti-corrosive performance, roughness and chemical composition of pre-treatment layer on the overall performance of the paint system on cold-rolled steel.pdf
格式: Adobe PDF
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。