Electrochemical Characteristics of an Austenitic Stainless Steel Under Simulated Solution Film Formed in Marine Atmosphere | |
Huang Yanliang; Dong Xiqing; Chen Jun; Huang, YL (reprint author), Chinese Acad Sci, Inst Oceanol, Qingdao 266071, Peoples R China | |
2011-11-01 | |
发表期刊 | INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE |
ISSN | 1452-3981 |
卷号 | 6期号:11页码:5597-5604 |
文章类型 | Article |
摘要 | Stainless structures and fasteners can fail as a result of stress corrosion cracking (SCC) in coastal atmosphere. In order to have a better understanding of the marine atmospheric SCC mechanism, the corrosion electrochemistry and hydrogen permeation behavior of stainless steel under surface solution film were studied. The solution film was more easily formed on the surface that was contaminated by alien substances such as rust of carbon steels. The stability of the passive film decreases with the development of the surface solution film and both the pitting potential and the SCC sensitive range shift to lower potentials. The hydrogen entry through stainless steel membrane during cyclic wet-dry corrosion conditions was also detected.; Stainless structures and fasteners can fail as a result of stress corrosion cracking (SCC) in coastal atmosphere. In order to have a better understanding of the marine atmospheric SCC mechanism, the corrosion electrochemistry and hydrogen permeation behavior of stainless steel under surface solution film were studied. The solution film was more easily formed on the surface that was contaminated by alien substances such as rust of carbon steels. The stability of the passive film decreases with the development of the surface solution film and both the pitting potential and the SCC sensitive range shift to lower potentials. The hydrogen entry through stainless steel membrane during cyclic wet-dry corrosion conditions was also detected. |
关键词 | Austenitic Stainless Steel Marine Atmosphere Corrosion Electrochemistry |
学科领域 | Electrochemistry |
收录类别 | SCI |
语种 | 英语 |
WOS记录号 | WOS:000297503300039 |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | http://ir.qdio.ac.cn/handle/337002/11441 |
专题 | 海洋环境腐蚀与生物污损重点实验室 |
通讯作者 | Huang, YL (reprint author), Chinese Acad Sci, Inst Oceanol, Qingdao 266071, Peoples R China |
作者单位 | Chinese Acad Sci, Inst Oceanol, Qingdao 266071, Peoples R China |
第一作者单位 | 中国科学院海洋研究所 |
推荐引用方式 GB/T 7714 | Huang Yanliang,Dong Xiqing,Chen Jun,et al. Electrochemical Characteristics of an Austenitic Stainless Steel Under Simulated Solution Film Formed in Marine Atmosphere[J]. INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE,2011,6(11):5597-5604. |
APA | Huang Yanliang,Dong Xiqing,Chen Jun,&Huang, YL .(2011).Electrochemical Characteristics of an Austenitic Stainless Steel Under Simulated Solution Film Formed in Marine Atmosphere.INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE,6(11),5597-5604. |
MLA | Huang Yanliang,et al."Electrochemical Characteristics of an Austenitic Stainless Steel Under Simulated Solution Film Formed in Marine Atmosphere".INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE 6.11(2011):5597-5604. |
条目包含的文件 | ||||||
文件名称/大小 | 文献类型 | 版本类型 | 开放类型 | 使用许可 | ||
Electrochemical Char(2019KB) | 限制开放 | -- | 浏览 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论